- 缺口冲击强度: 0.267
- 断裂伸长率 [%]: 107.49
- 弯曲强度 [MPa]: 66.32
- 弯曲模量 [MPa]: 2.785
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 1.0 cP | 1.0 cP | 50-12 water-like viscosity | ||
| 4000 - 6000 cP | 4000 - 6000 cP | 50-6 | |||
| 900 cP @Temperature 25.0 °C | 900 cP @Temperature 77.0 °F | at 100/14 (50-6/50-12) pbw | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 107 | 107 | |||
| Tensile Strength, Ultimate | 66.32 MPa | 9619 psi | |||
| Elongation at Break | 4.4 % | 4.4 % | |||
| Flexural Yield Strength | 107.49 MPa | 15590 psi | |||
| Flexural Modulus | 2.785 GPa | 403.9 ksi | |||
| Compressive Yield Strength | 109.21 MPa | 15840 psi | |||
| Compressive Modulus | 1.81 GPa | 263 ksi | |||
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.29e+16 ohm-cm | 1.29e+16 ohm-cm | |||
| Surface Resistance | 7.85e+14 ohm | 7.85e+14 ohm | |||
| Dielectric Constant | 3.27 @Frequency 1e+6 Hz | 3.27 @Frequency 1e+6 Hz | |||
| 3.86 @Frequency 1000 Hz | 3.86 @Frequency 1000 Hz | ||||
| 3.98 @Frequency 60 Hz | 3.98 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.010 @Frequency 60 Hz | 0.010 @Frequency 60 Hz | |||
| 0.027 @Frequency 1000 Hz | 0.027 @Frequency 1000 Hz | ||||
| 0.031 @Frequency 1e+6 Hz | 0.031 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 107 °C | 225 °F | Deflection temperature; load unknown. | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 43 min | 43 min | 500 g | ||
| Descriptive Properties | |||||
| Exotherm | 283°C | Peak | |||