- 缺口冲击强度: 0.267
- 断裂伸长率 [%]: 66.88
- 弯曲强度 [MPa]: 57.22
- 弯曲模量 [MPa]: 2.41
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 11000 - 14000 cP | 11000 - 14000 cP | 50-3 | ||
| 14000 - 20000 cP | 14000 - 20000 cP | 50-1 | |||
| 16000 cP @Temperature 25.0 °C | 16000 cP @Temperature 77.0 °F | at 100/35 (50-3/50-1) pbw | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 80 | 80 | |||
| Tensile Strength, Ultimate | 57.22 MPa | 8299 psi | |||
| Elongation at Break | 3.9 % | 3.9 % | |||
| Flexural Yield Strength | 66.88 MPa | 9700 psi | |||
| Flexural Modulus | 2.41 GPa | 350 ksi | |||
| Compressive Yield Strength | 85.49 MPa | 12400 psi | |||
| Compressive Modulus | 2.55 GPa | 370 ksi | |||
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.22e+16 ohm-cm | 1.22e+16 ohm-cm | |||
| Surface Resistance | 5.50e+15 ohm | 5.50e+15 ohm | |||
| Dielectric Constant | 2.99 @Frequency 1e+6 Hz | 2.99 @Frequency 1e+6 Hz | |||
| 3.19 @Frequency 1000 Hz | 3.19 @Frequency 1000 Hz | ||||
| 3.23 @Frequency 60 Hz | 3.23 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.0036 @Frequency 60 Hz | 0.0036 @Frequency 60 Hz | |||
| 0.0070 @Frequency 1000 Hz | 0.0070 @Frequency 1000 Hz | ||||
| 0.019 @Frequency 1e+6 Hz | 0.019 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 100 - 110 °C | 212 - 230 °F | Heat distortion temperature | ||
| 105 °C | 221 °F | Deflection temperature; load unknown. | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 140 min | 140 min | 500 g | ||
| Descriptive Properties | |||||
| Exotherm | 152°C | Peak | |||