- 断裂伸长率 [%]: 81.56
- 弯曲强度 [MPa]: 73.84
- 弯曲模量 [MPa]: 2.79
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity Measurement | 400 | 400 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 96 | 96 | |||
| Tensile Strength, Ultimate | 73.84 MPa | 10710 psi | |||
| Elongation at Break | 7.5 % | 7.5 % | |||
| Flexural Yield Strength | 81.56 MPa | 11830 psi | |||
| Flexural Modulus | 2.79 GPa | 405 ksi | |||
| Compressive Yield Strength | 98.25 MPa | 14250 psi | |||
| Compressive Modulus | 2.10 GPa | 305 ksi | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.19e+16 ohm-cm | 1.19e+16 ohm-cm | |||
| Surface Resistance | >= 1.19e+16 ohm | >= 1.19e+16 ohm | |||
| Dielectric Constant | 3.31 @Frequency 1e+6 Hz | 3.31 @Frequency 1e+6 Hz | |||
| 3.77 @Frequency 1000 Hz | 3.77 @Frequency 1000 Hz | ||||
| 3.84 @Frequency 60 Hz | 3.84 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.0079 @Frequency 60 Hz | 0.0079 @Frequency 60 Hz | |||
| 0.017 @Frequency 1000 Hz | 0.017 @Frequency 1000 Hz | ||||
| 0.028 @Frequency 1e+6 Hz | 0.028 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 84.0 °C | 183 °F | Deflection temperature; load unknown. | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 36 min | 36 min | 500 g | ||
| Descriptive Properties | |||||
| Exotherm | 265°C | Peak | |||