- 缺口冲击强度: 0.267
- 断裂伸长率 [%]: 95.83
- 弯曲强度 [MPa]: 78.6
- 弯曲模量 [MPa]: 3.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 1.0 cP | 1.0 cP | 50-12 water-like viscosity | ||
| 11000 - 14000 cP | 11000 - 14000 cP | 50-3 | |||
| 2250 cP @Temperature 25.0 °C | 2250 cP @Temperature 77.0 °F | at 100/13 (50-3/50-12) pbw | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 106 | 106 | |||
| Tensile Strength, Ultimate | 78.6 MPa | 11400 psi | |||
| Elongation at Break | 4.4 % | 4.4 % | |||
| Flexural Yield Strength | 95.83 MPa | 13900 psi | |||
| Flexural Modulus | 3.00 GPa | 435 ksi | |||
| Compressive Yield Strength | 112.38 MPa | 16299 psi | |||
| Compressive Modulus | 3.03 GPa | 440 ksi | |||
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 6.10e+15 ohm-cm | 6.10e+15 ohm-cm | |||
| Surface Resistance | 7.85e+15 ohm | 7.85e+15 ohm | |||
| Dielectric Constant | 3.42 @Frequency 1e+6 Hz | 3.42 @Frequency 1e+6 Hz | |||
| 3.9 @Frequency 1000 Hz | 3.9 @Frequency 1000 Hz | ||||
| 4.02 @Frequency 60 Hz | 4.02 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.0074 @Frequency 60 Hz | 0.0074 @Frequency 60 Hz | |||
| 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | ||||
| 0.032 @Frequency 1e+6 Hz | 0.032 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 111 °C | 232 °F | Deflection temperature; load unknown. | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 30 min | 30 min | 500 g | ||
| Descriptive Properties | |||||
| Exotherm | 255°C | Peak | |||