| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | |||
| Viscosity | 12000 cP | 12000 cP | Mixed Viscosity | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 70 | 70 | |||
| Flexural Strength | 55.2 MPa | 8000 psi | ASTM D790 | ||
| Shear Strength | 8.27 MPa | 1200 psi | ASTM D1002-94 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | |||
| Dielectric Constant | 6.0 @Frequency 1000 Hz | 6.0 @Frequency 1000 Hz | |||
| Dielectric Strength | 33.9 kV/mm | 860 kV/in | |||
| Dissipation Factor | 0.040 | 0.040 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 28.8 µm/m-°C @Temperature 20.0 °C | 16.0 µin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 200 °C | 392 °F | |||
| Minimum Service Temperature, Air | -50.0 °C | -58.0 °F | |||
| Shrinkage | 0.80 % | 0.80 % | Cure Shrinkage | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 min | 0.500 hour | at 200°F (Alternate Cure) | ||
| 45.0 min | 0.750 hour | Room Temperature (Recommended Cure) | |||
| Pot Life | 15 min | 15 min | 100 gm mass @ 25°C | ||
| Descriptive Properties | |||||
| Chemical Resistance | Excellent | ||||
| Mix Ratio by Weight | 1:1 | resin:hardener | |||