| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.850 g/cc | 0.850 g/cc | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 75 | 75 | |||
| Flexural Strength | 78.6 MPa | 11400 psi | ASTM D790 | ||
| Shear Strength | 17.2 MPa | 2500 psi | ASTM D1002-94 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 100000 ohm-cm | 100000 ohm-cm | |||
| Dielectric Strength | 3.15 kV/mm | 80.0 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 59.4 µm/m-°C @Temperature 20.0 °C | 33.0 µin/in-°F @Temperature 68.0 °F | |||
| Thermal Conductivity | 1.30 W/m-K | 9.00 BTU-in/hr-ft²-°F | |||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -65.0 °C | -85.0 °F | |||
| Shrinkage | 0.20 % | 0.20 % | Cure Shrinkage | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min | 2.00 hour | at 200°F (Recommended Cure) | ||
| 1440 - 2880 min | 24.0 - 48.0 hour | Room Temperature (Alternate Cure) | |||
| Pot Life | 240 min | 240 min | 100 gm mass @ 25°C | ||
| Descriptive Properties | |||||
| Chemical Resistance | Excellent | ||||
| Mix Ratio by Weight | 1:1 | resin:hardener | |||