- 弯曲强度 [MPa]: 59.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 1000 cP | 1000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 82 | 82 | |||
| Tensile Strength, Ultimate | 59.0 MPa | 8550 psi | after optimum cure | ||
| Elongation at Break | 4.3 % | 4.3 % | |||
| Adhesive Bond Strength | 44.8 MPa | 6500 psi | Steel-Steel; after optimum cure | ||
| 11.0 MPa @Temperature 25.0 °C | 1600 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| 13.8 MPa @Temperature -54.4 °C | 2000 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 16.2 MPa @Temperature 82.2 °C | 2350 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 34.0 µm/m-°C @Temperature 20.0 °C | 18.9 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 100 °C | 212 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 93.3 °C | 200 °F | Optimum cure is 1 hr. @ 200°F | ||
| Pot Life | 120 - 180 min | 120 - 180 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Amber | ||||
| Mix Ratio | 100/12 | By Weight | |||