- 弯曲强度 [MPa]: 179.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | |||
| Brookfield Viscosity | 3600 cP @Temperature 23.9 °C | 3600 cP @Temperature 75.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 90 @Temperature 23.9 °C | 90 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 179 MPa | 26000 psi | 10 oz glass cloth laminate | ||
| Flexural Strength | 228 MPa | 33000 psi | 10 oz glass cloth laminate | ||
| Compressive Strength | 364 MPa | 52800 psi | 10 oz glass cloth laminate | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 22.9 µm/m-°C | 12.7 µin/in-°F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 1440 min @Temperature 24.0 °C | 24.0 hour @Temperature 75.2 °F | |||
| Pot Life | 60 min @Temperature 24.0 °C | 60 min @Temperature 75.2 °F | 1 lb. mass | ||
| Descriptive Properties | |||||
| Mix Ratio | 100:13 by weight, 100:18 by volume, resin/harder | ||||