- 弯曲强度 [MPa]: 58.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 24000 cP | 24000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 82 | 82 | |||
| Tensile Strength, Ultimate | 58.6 MPa | 8500 psi | after optimum cure | ||
| Elongation at Break | 3.7 % | 3.7 % | |||
| Adhesive Bond Strength | 26.2 MPa | 3800 psi | Steel-Steel; after optimum cure | ||
| 14.1 MPa @Temperature 25.0 °C | 2050 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| 14.5 MPa @Temperature 82.2 °C | 2100 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 15.2 MPa @Temperature -54.4 °C | 2200 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C | 22.2 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 98.0 °C | 208 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 73.9 °C | 165 °F | Optimum cure is 2 hr. @ 165°F | |||
| 149 °C | 300 °F | Fast cure is 5 min. @ 300°F | |||
| Pot Life | 45 min | 45 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Amber | ||||
| Mix Ratio | 3/1 | By Weight | |||