- 弯曲强度 [MPa]: 47.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 250000 cP | 250000 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 88 | 88 | |||
| Tensile Strength, Ultimate | 47.2 MPa | 6850 psi | after optimum cure | ||
| Elongation at Break | 1.9 % | 1.9 % | |||
| Adhesive Bond Strength | 65.5 MPa | 9500 psi | Steel-Steel; after optimum cure | ||
| 30.3 MPa @Temperature -54.4 °C | 4400 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 31.0 MPa @Temperature 82.2 °C | 4500 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 40.3 MPa @Temperature 25.0 °C | 5850 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 53.0 µm/m-°C @Temperature 20.0 °C | 29.4 µin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Glass Transition Temp, Tg | 171 °C | 340 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 204 °C | 400 °F | Optimum cure is 1 hr. @ 400°F | ||
| Pot Life | 99999 min | 99999 min | Indefinite working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Grey | ||||
| Mix Ratio | 1 Part | ||||