- 弯曲强度 [MPa]: 41.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 22000 cP | 22000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 78 | 78 | |||
| Tensile Strength, Ultimate | 41.0 MPa | 5940 psi | after optimum cure | ||
| Elongation at Break | 5.6 % | 5.6 % | |||
| Adhesive Bond Strength | 36.5 MPa | 5300 psi | Steel-Steel; after optimum cure | ||
| 9.31 MPa @Temperature 82.2 °C | 1350 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 19.3 MPa @Temperature -54.4 °C | 2800 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 21.0 MPa @Temperature 25.0 °C | 3050 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 73.0 µm/m-°C @Temperature 20.0 °C | 40.6 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 55.0 °C | 131 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 93.3 °C | 200 °F | Optimum cure is 15 min. @ 200°F | |||
| 149 °C | 300 °F | Fast cure is 5 min. @ 300°F | |||
| Pot Life | 90 min | 90 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Amber | ||||
| Mix Ratio | 1/1 | By Weight | |||