- 弯曲强度 [MPa]: 42.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 16000 cP | 16000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 80 | 80 | |||
| Tensile Strength, Ultimate | 42.1 MPa | 6100 psi | after optimum cure | ||
| Elongation at Break | 4.9 % | 4.9 % | |||
| Adhesive Bond Strength | 31.0 MPa | 4500 psi | Steel-Steel; after optimum cure | ||
| 11.0 MPa @Temperature 82.2 °C | 1600 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 20.7 MPa @Temperature -54.4 °C | 3000 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 24.8 MPa @Temperature 25.0 °C | 3600 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 33.0 µm/m-°C @Temperature 20.0 °C | 18.3 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 68.0 °C | 154 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 93.3 °C | 200 °F | Optimum cure is 15 min. @ 200°F | |||
| 149 °C | 300 °F | Fast cure is 5 min. @ 300°F | |||
| Pot Life | 90 min | 90 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Amber | ||||
| Mix Ratio | 3/2 | By Weight | |||