- 弯曲强度 [MPa]: 37.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 400000 cP | 400000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 83 | 83 | |||
| Tensile Strength, Ultimate | 37.9 MPa | 5500 psi | after optimum cure | ||
| Elongation at Break | 2.0 % | 2.0 % | |||
| Adhesive Bond Strength | 51.4 MPa | 7450 psi | Steel-Steel; after optimum cure | ||
| 15.9 MPa @Temperature 82.2 °C | 2300 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 19.3 MPa @Temperature -54.4 °C | 2800 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 19.7 MPa @Temperature 25.0 °C | 2850 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 34.0 µm/m-°C @Temperature 20.0 °C | 18.9 µin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 121 °C | 250 °F | |||
| Glass Transition Temp, Tg | 77.0 °C | 171 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 73.9 °C | 165 °F | Optimum cure is 30 min. @ 165°F | |||
| 149 °C | 300 °F | Fast cure is 10 min. @ 300°F | |||
| Pot Life | 120 min | 120 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Brown | ||||
| Mix Ratio | 4/1 | By Weight | |||