- 弯曲强度 [MPa]: 59.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 1500 cP | 1500 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 84 | 84 | |||
| Tensile Strength, Ultimate | 59.3 MPa | 8600 psi | after optimum cure | ||
| Elongation at Break | 3.2 % | 3.2 % | |||
| Adhesive Bond Strength | 30.0 MPa | 4350 psi | Steel-Steel; after optimum cure | ||
| 9.65 MPa @Temperature 25.0 °C | 1400 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| 13.4 MPa @Temperature 82.2 °C | 1950 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 15.5 MPa @Temperature -54.4 °C | 2250 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 32.0 µm/m-°C @Temperature 20.0 °C | 17.8 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 115 °C | 239 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 73.9 °C | 165 °F | Optimum cure is 2 hr. @ 165°F | |||
| 149 °C | 300 °F | Fast cure is 5 min. @ 300°F | |||
| Pot Life | 40 min | 40 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Amber | ||||
| Mix Ratio | 4/1 | By Weight | |||