- 弯曲强度 [MPa]: 53.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 2200 cP | 2200 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 80 | 80 | |||
| Tensile Strength, Ultimate | 53.1 MPa | 7700 psi | after optimum cure | ||
| Elongation at Break | 4.8 % | 4.8 % | |||
| Adhesive Bond Strength | 43.4 MPa | 6300 psi | Steel-Steel; after optimum cure | ||
| 7.58 MPa @Temperature 82.2 °C | 1100 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 16.2 MPa @Temperature 25.0 °C | 2350 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| 16.9 MPa @Temperature -54.4 °C | 2450 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C | 20.0 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 79.0 °C | 174 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 73.9 °C | 165 °F | Optimum cure is 2 hr. @ 165°F | |||
| 149 °C | 300 °F | Fast cure is 30 min. @ 300°F | |||
| Pot Life | 40 min | 40 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Amber | ||||
| Mix Ratio | 3/1 | By Weight | |||