- 弯曲强度 [MPa]: 36.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 430000 cP | 430000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 86 | 86 | |||
| Tensile Strength, Ultimate | 36.5 MPa | 5300 psi | after optimum cure | ||
| Elongation at Break | 1.3 % | 1.3 % | |||
| Adhesive Bond Strength | 32.4 MPa | 4700 psi | Steel-Steel; after optimum cure | ||
| 16.5 MPa @Temperature -54.4 °C | 2400 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 16.5 MPa @Temperature 25.0 °C | 2400 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| 19.0 MPa @Temperature 82.2 °C | 2750 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 34.0 µm/m-°C @Temperature 20.0 °C | 18.9 µin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 121 °C | 250 °F | |||
| Glass Transition Temp, Tg | 103 °C | 217 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 73.9 °C | 165 °F | Optimum cure is 2 hr. @ 165°F | |||
| Pot Life | 30 min | 30 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Brown | ||||
| Mix Ratio | 100/4 | By Weight | |||