- 弯曲强度 [MPa]: 23.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 850000 cP | 850000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 84 | 84 | |||
| Tensile Strength, Ultimate | 23.1 MPa | 3350 psi | after optimum cure | ||
| Elongation at Break | 1.6 % | 1.6 % | |||
| Adhesive Bond Strength | 53.4 MPa | 7750 psi | Steel-Steel; after optimum cure | ||
| 11.0 MPa @Temperature 25.0 °C | 1600 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| 12.4 MPa @Temperature -54.4 °C | 1800 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 17.6 MPa @Temperature 82.2 °C | 2550 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 48.0 µm/m-°C @Temperature 20.0 °C | 26.7 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 86.0 °C | 187 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 73.9 °C | 165 °F | Optimum cure is 2 hr. @ 165°F | |||
| Pot Life | 30 min | 30 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Grey | ||||
| Mix Ratio | 100/4 | By Weight | |||