- 弯曲强度 [MPa]: 31.4
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 280000 cP | 280000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 84 | 84 | |||
| Tensile Strength, Ultimate | 31.4 MPa | 4550 psi | after optimum cure | ||
| Elongation at Break | 2.1 % | 2.1 % | |||
| Adhesive Bond Strength | 26.9 MPa | 3900 psi | Steel-Steel; after optimum cure | ||
| 6.55 MPa @Temperature 82.2 °C | 950 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 10.0 MPa @Temperature -54.4 °C | 1450 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 25.9 MPa @Temperature 25.0 °C | 3750 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 61.0 °C | 142 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 93.3 °C | 200 °F | Optimum cure is 30 min. @ 200°F | |||
| 149 °C | 300 °F | Fast cure is 5 min. @ 300°F | |||
| Pot Life | 20 min | 20 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | White | ||||
| Mix Ratio | 1/1 | By Weight | |||