- 弯曲强度 [MPa]: 29.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 13000 cP | 13000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 75 | 75 | |||
| Tensile Strength, Ultimate | 29.0 MPa | 4200 psi | after optimum cure | ||
| Elongation at Break | 1.8 % | 1.8 % | |||
| Adhesive Bond Strength | 53.8 MPa | 7800 psi | Steel-Steel; after optimum cure | ||
| 11.4 MPa @Temperature 25.0 °C | 1650 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| 14.8 MPa @Temperature -54.4 °C | 2150 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 17.2 MPa @Temperature 82.2 °C | 2500 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 69.0 µm/m-°C @Temperature 20.0 °C | 38.3 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 100 °C | 212 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 93.3 °C | 200 °F | Optimum cure is 1 hr. @ 200°F | ||
| Pot Life | 120 - 180 min | 120 - 180 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Silver | ||||
| Mix Ratio | 100/10 | By Weight | |||