- 弯曲强度 [MPa]: 37.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 20000 cP | 20000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 50 | 50 | |||
| Tensile Strength, Ultimate | 37.9 MPa | 5500 psi | after optimum cure | ||
| Elongation at Break | 8.0 % | 8.0 % | |||
| Adhesive Bond Strength | 35.2 MPa | 5100 psi | Steel-Steel; after optimum cure | ||
| 11.7 MPa @Temperature 82.2 °C | 1700 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 16.9 MPa @Temperature -54.4 °C | 2450 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 24.8 MPa @Temperature 25.0 °C | 3600 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 65.0 µm/m-°C @Temperature 20.0 °C | 36.1 µin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 121 °C | 250 °F | |||
| Minimum Service Temperature, Air | -53.9 °C | -65.0 °F | |||
| Glass Transition Temp, Tg | 55.0 °C | 131 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 73.9 °C | 165 °F | Optimum cure is 20 min. @ 165°F | |||
| Pot Life | 5.0 min | 5.0 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Clear | ||||
| Mix Ratio | 100/100 | By Weight | |||