- 弯曲强度 [MPa]: 43.8
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore D | 82 | 82 | |||
| Tensile Strength, Ultimate | 43.8 MPa | 6350 psi | after optimum cure | ||
| Elongation at Break | 2.5 % | 2.5 % | |||
| Adhesive Bond Strength | 34.8 MPa | 5050 psi | Steel-Steel; after optimum cure | ||
| 17.2 MPa @Temperature -54.4 °C | 2500 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 22.8 MPa @Temperature 82.2 °C | 3300 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 26.9 MPa @Temperature 25.0 °C | 3900 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 35.0 µm/m-°C @Temperature 20.0 °C | 19.4 µin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Glass Transition Temp, Tg | 115 °C | 239 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 149 °C | 300 °F | Optimum cure is 10 min. @ 300°F | |||
| Pot Life | 180 min | 180 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Off White | ||||
| Mix Ratio | 4/1 | By Weight | |||