- 弯曲强度 [MPa]: 43.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 170000 cP | 170000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 87 | 87 | |||
| Tensile Strength, Ultimate | 43.8 MPa | 6350 psi | after optimum cure | ||
| Elongation at Break | 3.7 % | 3.7 % | |||
| Adhesive Bond Strength | 59.0 MPa | 8550 psi | Steel-Steel; after optimum cure | ||
| 15.9 MPa @Temperature -54.4 °C | 2300 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 17.9 MPa @Temperature 82.2 °C | 2600 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 21.4 MPa @Temperature 25.0 °C | 3100 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 55.0 µm/m-°C @Temperature 20.0 °C | 30.6 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 84.0 °C | 183 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 93.3 °C | 200 °F | Optimum cure is 1 hr. @ 200°F | ||
| Pot Life | 90 min | 90 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | White | ||||
| Mix Ratio | 100/6 | By Weight | |||