- 弯曲强度 [MPa]: 38.6
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore D | 74 | 74 | |||
| Tensile Strength, Ultimate | 38.6 MPa | 5600 psi | after optimum cure | ||
| Elongation at Break | 4.0 % | 4.0 % | |||
| Adhesive Bond Strength | 32.8 MPa | 4750 psi | Steel-Steel; after optimum cure | ||
| 13.4 MPa @Temperature -54.4 °C | 1940 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 14.5 MPa @Temperature 82.2 °C | 2100 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 25.2 MPa @Temperature 25.0 °C | 3650 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 72.0 µm/m-°C @Temperature 20.0 °C | 40.0 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 63.0 °C | 145 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 73.9 °C | 165 °F | Optimum cure is 20 min. @ 165°F | |||
| Pot Life | 5.0 min | 5.0 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Clear Straw | ||||
| Mix Ratio | 100/100 | By Weight | |||