- 密度 [g/cm3]: 1.75
- 吸水率 [%]: 0.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in³ | ASTM D792 Method A | ||
| Water Absorption | 0.10 % | 0.10 % | IPC TM-650 2.6.2.1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Modulus of Elasticity | 17.9 GPa | 2600 ksi | IPC TM-650 2.4.18.3 | ||
| Flexural Strength | 579 MPa | 84000 psi | IPC TM-650 2.4.4 | ||
| Poissons Ratio | 0.17 | 0.17 | ASTM D3039 | ||
| Peel Strength | 1.58 kN/m | 9.00 pli | After Thermal Stress; IPC TM-650 2.4.8 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.30e+12 ohm-cm | 3.30e+12 ohm-cm | E24/125; IPC TM-650 2.5.17.1 | ||
| 2.60e+13 ohm-cm | 2.60e+13 ohm-cm | C96/35/90; IPC TM-650 2.5.17.1 | |||
| Surface Resistance | 4.00e+12 ohm | 4.00e+12 ohm | E24/125; IPC TM-650 2.5.17.1 | ||
| 2.90e+13 ohm | 2.90e+13 ohm | C96/35/90; IPC TM-650 2.5.17.1 | |||
| Dielectric Constant | 4.4 @Frequency 1.00e+6 Hz | 4.4 @Frequency 1.00e+6 Hz | IPC TM-650 2.5.5.3 | ||
| Dielectric Strength | 39.4 kV/mm | 1000 kV/in | IPC TM-650 2.5.6.2 | ||
| Dissipation Factor | 0.025 @Frequency 1.00e+6 Hz | 0.025 @Frequency 1.00e+6 Hz | IPC TM-650 2.5.5.3 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 14.0 - 16.0 µm/m-°C | 7.78 - 8.89 µin/in-°F | IPC TM-650 2.4.41 | ||
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C | 48.3 µin/in-°F | z, below Tg; IPC TM-650 2.4.24 | ||
| 246 µm/m-°C | 137 µin/in-°F | z, above Tg; IPC TM-650 2.4.24 | |||
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | ASTM E1461 | ||
| Glass Transition Temp, Tg | 170 °C | 338 °F | DSC; IPC TM-650 2.4.25 | ||
| Decomposition Temperature | 291 °C | 556 °F | Onset; IPC TM-650 2.3.41 | ||
| 302 °C | 576 °F | 5 percent; IPC TM-650 2.3.41 | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Descriptive Properties | |||||
| IPC Delamination - T260 (minutes) | 10 | IPC TM-650 2.4.24.1 | |||
| IPC Delamination - T288 (minutes) | 0 | IPC TM-650 2.4.24.1 | |||
| IPC Delamination - T300 (minutes) | 0 | IPC TM-650 2.4.24.1 | |||
| Z-Axis Expansion (%) | 3.1 | IPC TM-650 2.4.24 (50-260°C) | |||