- 弯曲强度 [MPa]: 34.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 15000 cP | 15000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 84 | 84 | |||
| Tensile Strength, Ultimate | 34.5 MPa | 5000 psi | after optimum cure | ||
| Elongation at Break | 1.9 % | 1.9 % | |||
| Adhesive Bond Strength | 44.5 MPa | 6450 psi | Steel-Steel; after optimum cure | ||
| 6.89 MPa @Temperature 82.2 °C | 1000 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 10.3 MPa @Temperature -54.4 °C | 1500 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 12.1 MPa @Temperature 25.0 °C | 1750 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 58.0 µm/m-°C @Temperature 20.0 °C | 32.2 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 58.0 °C | 136 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 93.3 °C | 200 °F | Fast cure is 10 min. @ 200°F | |||
| 93.3 °C | 200 °F | Optimum cure is 30 min. @ 200°F | |||
| Pot Life | 90 min | 90 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | White | ||||
| Mix Ratio | 10/1 | By Weight | |||