- 弯曲强度 [MPa]: 37.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 80000 cP | 80000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 82 | 82 | |||
| Tensile Strength, Ultimate | 37.6 MPa | 5450 psi | after optimum cure | ||
| Elongation at Break | 2.4 % | 2.4 % | |||
| Adhesive Bond Strength | 34.5 MPa | 5000 psi | Steel-Steel; after optimum cure | ||
| 20.3 MPa @Temperature -54.4 °C | 2950 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 23.4 MPa @Temperature 25.0 °C | 3400 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| 23.4 MPa @Temperature 82.2 °C | 3400 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 35.0 µm/m-°C @Temperature 20.0 °C | 19.4 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 83.0 °C | 181 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 93.3 °C | 200 °F | Optimum cure is 20 min. @ 200°F | |||
| 149 °C | 300 °F | Fast cure is 5 min. @ 300°F | |||
| Pot Life | 90 min | 90 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Brown | ||||
| Mix Ratio | 3/2 | By Weight | |||