- 弯曲强度 [MPa]: 49.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.83 g/cc | 2.83 g/cc | |||
| Brookfield Viscosity | 10000 cP @Temperature 23.9 °C | 10000 cP @Temperature 75.0 °F | Mixed | ||
| Linear Mold Shrinkage | 0.00020 cm/cm | 0.00020 in/in | ASTM D2566-69 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 90 @Temperature 23.9 °C | 90 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 49.6 MPa | 7200 psi | |||
| Flexural Strength | 62.1 MPa | 9000 psi | |||
| Compressive Strength | 106 MPa | 15400 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 57.6 µm/m-°C | 32.0 µin/in-°F | |||
| Heat Distortion Temperature | 52.8 °C | 127 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 720 - 1080 min @Temperature 24.0 °C | 12.0 - 18.0 hour @Temperature 75.2 °F | |||
| 10080 min @Temperature 24.0 °C | 168.0 hour @Temperature 75.2 °F | complete cure | |||
| Pot Life | 55 - 60 min @Temperature 24.0 °C | 55 - 60 min @Temperature 75.2 °F | 1 lb. mass | ||
| Descriptive Properties | |||||
| Machinability | Good | ||||
| Mix Ratio | 100:5 by weight, 100:6.5 by volume, resin/harder | ||||