- 弯曲强度 [MPa]: 36.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | |||
| Brookfield Viscosity | 5400 cP @Temperature 23.9 °C | 5400 cP @Temperature 75.0 °F | Mixed | ||
| Linear Mold Shrinkage | 0.0012 cm/cm | 0.0012 in/in | ASTM D2566-69 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 86 @Temperature 23.9 °C | 86 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 36.5 MPa | 5300 psi | |||
| Flexural Strength | 60.7 MPa | 8800 psi | |||
| Compressive Strength | 99.3 MPa | 14400 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 57.6 µm/m-°C | 32.0 µin/in-°F | |||
| Heat Distortion Temperature | 56.7 °C | 134 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 720 - 1080 min @Temperature 24.0 °C | 12.0 - 18.0 hour @Temperature 75.2 °F | |||
| Pot Life | 50 - 60 min @Temperature 24.0 °C | 50 - 60 min @Temperature 75.2 °F | 2 lb. mass | ||
| Descriptive Properties | |||||
| Machinability | Excellent | ||||
| Mix Ratio | 12:1 by weight, 6.5:1 by volume, resin/harder | ||||