- 弯曲强度 [MPa]: 173.0
- 弯曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | |||
| Brookfield Viscosity | 3200 cP @Temperature 25.0 °C | 3200 cP @Temperature 77.0 °F | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 90 @Temperature 25.0 °C | 90 @Temperature 77.0 °F | |||
| Tensile Strength, Ultimate | 173 MPa | 25100 psi | |||
| Flexural Strength | 210 MPa | 30500 psi | |||
| Flexural Modulus | 13.0 GPa | 1880 ksi | |||
| Compressive Strength | 266 MPa | 38600 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 23.4 µm/m-°C | 13.0 µin/in-°F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 480 - 720 min @Temperature 24.0 °C | 8.00 - 12.0 hour @Temperature 75.2 °F | |||
| Pot Life | 25 - 30 min @Temperature 24.0 °C | 25 - 30 min @Temperature 75.2 °F | 1 lb. mass | ||
| Descriptive Properties | |||||
| Mix Ratio | 6:1 by weight, 4.5:1 by volume, resin/harder | ||||