- 弯曲强度 [MPa]: 42.7
- 弯曲模量 [MPa]: 6.76
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.24 g/cc | 2.24 g/cc | |||
| Brookfield Viscosity | 20000 cP @Temperature 23.9 °C | 20000 cP @Temperature 75.0 °F | Mixed | ||
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 87 @Temperature 23.9 °C | 87 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 42.7 MPa | 6200 psi | |||
| Flexural Strength | 53.8 MPa | 7800 psi | |||
| Flexural Modulus | 6.76 GPa | 980 ksi | |||
| Compressive Strength | 102 MPa | 14800 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.9 °C | 138 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 960 min @Temperature 24.0 °C | 16.0 hour @Temperature 75.2 °F | |||
| Pot Life | 90 min @Temperature 24.0 °C | 90 min @Temperature 75.2 °F | 2 lb. mass | ||
| Descriptive Properties | |||||
| Machinability | Good | ||||
| Mix Ratio | 100:10 by weight, 100:26 by volume, resin/harder | ||||