- 密度 [g/cm3]: 1.45
- 弯曲强度 [MPa]: 51.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 - 1.51 g/cc | 0.0524 - 0.0546 lb/in³ | |
| Solids Content | >= 98 % | >= 98 % | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | DIN 53 504 |
| Elongation at Break | 1.3 % | 1.3 % | DIN 53 504 |
| Modulus of Elasticity | 6.60 GPa | 957 ksi | DIN 53 504 |
| Adhesive Bond Strength | 15.0 MPa @Thickness 0.750 mm | 2180 psi @Thickness 0.0295 in | Lap Shear (CRS St 1203); EN 1465 |
| 20.0 MPa @Thickness 1.50 mm | 2900 psi @Thickness 0.0591 in | Lap Shear (CRS St 1203); EN 1465 | |
| Peel Strength | 2.00 kN/m | 11.4 pli | T-Peel (CRS St 1203, 0.5mm) |
| 3.40 kN/m | 19.4 pli | Impact Peel | |
| Thermal Properties | Metric | English | Comments |
| Flash Point | 245 °C | 473 °F | |
| Processing Properties | Metric | English | Comments |
| Extrusion Rate | 78.0 g/min | 78.0 g/min | 3 bar, 3mm aperture |
| Cure Time | 30.0 min | 0.500 hour | 180°C |