- 密度 [g/cm3]: 0.752
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.752 g/cc | 0.0272 lb/in³ | Polymer Cured Physical Property | ||
| Mechanical Properties | Metric | English | Comments | ||
| Modulus of Elasticity | 1.47 GPa | 213 ksi | Polymer Cured Physical Property | ||
| Poissons Ratio | 0.11 | 0.11 | Polymer Cured Physical Property | ||
| Shear Modulus | 0.662 GPa | 96.0 ksi | Calculated | ||
| Thermal Properties | Metric | English | Comments | ||
| Flash Point | >= 204 °C | >= 400 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 7.00 min | 0.117 hour | 320°F (160°C) | ||
| 30.0 min | 0.500 hour | 266°F (130°C) | |||
| Descriptive Properties | |||||
| Flexural Reinforcement Force N | 29 | 2mm deflection; 1.3mm thick; After 500 hrs @ 200°F | |||
| 32 | 2mm deflection; 1.9mm thick; After 500 hrs @ 200°F | ||||
| 37 | 2mm deflection; 1.3mm thick; After 14 days @ 190°F | ||||
| 37 | 2mm deflection; 1.3mm thick; After 500 hrs @ 100°F & 100% RH | ||||
| 38 | 2mm deflection; 1.3mm thick; Initial | ||||
| 54 | 2mm deflection; 1.9mm thick; After 500 hrs @ 100°F & 100% RH | ||||
| 57 | 2mm deflection; 1.9mm thick; Initial | ||||
| 57 | 2mm deflection; 1.9mm thick; After 14 days @ 190°F | ||||
| Max Load N | 180 | 1.3mm thick; 21mm max deflection | |||
| 255 | 1.9mm thick; 18mm max deflection | ||||