- 弯曲模量 [MPa]: 0.00350
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Storage Temperature | 23.0 °C | 73.4 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 97.0 MPa | 14100 psi | |||
| Elongation at Break | 4.6 % | 4.6 % | |||
| Tensile Modulus | 0.00370 GPa | 0.537 ksi | |||
| Flexural Modulus | 0.00350 GPa @Temperature 25.0 °C | 0.508 ksi @Temperature 77.0 °F | |||
| Flexural Stiffness | 146 MPa @Temperature 25.0 °C | 21200 psi @Temperature 77.0 °F | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 121 °C | 250 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 90.0 min @Temperature 180 °C | 1.50 hour @Temperature 356 °F | |||
| Descriptive Properties | |||||
| Consistency | Moderate Viscosity | ||||
| Form | 1 part | ||||
| Fracture Toughness (J/m2) | 471 | ||||
| Pot Life | 6 months | ||||