- 拉伸强度 [MPa]: 352.0
- 断裂伸长率 [%]: 1030
- 弯曲模量 [MPa]: 58.6
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 352 MPa @Temperature 25.0 °C | 51000 psi @Temperature 77.0 °F | Open Hole Tensile, Dry |
| 752 MPa @Temperature -55.0 °C | 109000 psi @Temperature -67.0 °F | 90°, Dry | |
| 772 MPa @Temperature 93.3 °C | 112000 psi @Temperature 200 °F | 90°, Dry | |
| 800 MPa @Temperature 25.0 °C | 116000 psi @Temperature 77.0 °F | 90°, Dry | |
| 827 MPa @Temperature -55.0 °C | 120000 psi @Temperature -67.0 °F | 0°, Dry | |
| 876 MPa @Temperature 25.0 °C | 127000 psi @Temperature 77.0 °F | 0°, Dry | |
| 903 MPa @Temperature 90.6 °C | 131000 psi @Temperature 195 °F | 0°, Dry | |
| Tensile Modulus | 64.8 GPa @Temperature 200 °C | 9400 ksi @Temperature 392 °F | 90°, Dry |
| 65.5 GPa @Temperature 77.0 °C | 9500 ksi @Temperature 171 °F | 90°, Dry | |
| 66.9 GPa @Temperature 77.0 °C | 9700 ksi @Temperature 171 °F | 0°, Dry | |
| 66.9 GPa @Temperature -67.0 °C | 9700 ksi @Temperature -88.6 °F | 90°, Dry | |
| 68.9 GPa @Temperature 195 °C | 10000 ksi @Temperature 383 °F | 0°, Dry | |
| 70.3 GPa @Temperature -67.0 °C | 10200 ksi @Temperature -88.6 °F | 0°, Dry | |
| Flexural Yield Strength | 1030 MPa @Temperature 25.0 °C | 150000 psi @Temperature 77.0 °F | 0°, Dry |
| Flexural Modulus | 58.6 GPa @Temperature 25.0 °C | 8500 ksi @Temperature 77.0 °F | 0°, Dry |
| Compressive Yield Strength | 281 MPa @Temperature 25.0 °C | 40800 psi @Temperature 77.0 °F | Compression After Impact, Dry |
| 370 MPa @Temperature 25.6 °C | 53700 psi @Temperature 78.0 °F | Open Hole Compression, Dry | |
| 510 MPa @Temperature 93.3 °C | 74000 psi @Temperature 200 °F | 0°, Wet | |
| 526 MPa @Temperature 25.0 °C | 76300 psi @Temperature 77.0 °F | Compression Before Impact, Dry | |
| 752 MPa @Temperature 93.3 °C | 109000 psi @Temperature 200 °F | 0°, Dry | |
| 889 MPa @Temperature 25.0 °C | 129000 psi @Temperature 77.0 °F | 0°, Dry, Fill Compression | |
| 924 MPa @Temperature 25.0 °C | 134000 psi @Temperature 77.0 °F | 0°, Dry | |
| 1030 MPa @Temperature -55.0 °C | 150000 psi @Temperature -67.0 °F | 0°, Dry, Fill Compression | |
| Compressive Modulus | 64.1 GPa @Temperature 25.0 °C | 9300 ksi @Temperature 77.0 °F | 0°, Dry |
| 66.9 GPa @Temperature 93.3 °C | 9700 ksi @Temperature 200 °F | 0°, Dry | |
| Shear Strength | 47.6 MPa @Temperature 93.3 °C | 6900 psi @Temperature 200 °F | 0° Short Beam, Dry |
| 68.9 MPa @Temperature 25.0 °C | 10000 psi @Temperature 77.0 °F | 0° Short Beam, Wet | |
| 78.6 MPa @Temperature 25.0 °C | 11400 psi @Temperature 77.0 °F | 0° Short Beam, Dry | |
| 80.7 MPa @Temperature 25.0 °C | 11700 psi @Temperature 77.0 °F | Fill Short Beam, Dry | |
| 94.5 MPa @Temperature -55.0 °C | 13700 psi @Temperature -67.0 °F | Fill Short Beam, Dry | |
| 110 MPa @Temperature 25.0 °C | 15900 psi @Temperature 77.0 °F | +/- 45° In-Plane, Dry | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 121 °C | 250 °F | Epoxy Matrix Limit |