- 密度 [g/cm3]: 0.98
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.980 g/cc | 0.0354 lb/in³ | |
| Density | 0.980 g/cc | 0.0354 lb/in³ | |
| Thickness | 381 microns | 15.0 mil | Nominal |
| 406 microns | 16.0 mil | Typical; ASTM D374 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 12.8 % | 12.8 % | ASTM D828 |
| Film Elongation at Break, TD | 16.5 % | 16.5 % | ASTM D828 |
| Flex Crack Resistance | 9200 | 9200 | Cycles of Fold Endurance; ASTM D2176 |
| Tear Strength, Total | 60.0 N | 13.5 lb (f) | Initial in TD; ASTM D1004 |
| 110 N | 24.7 lb (f) | Initial in MD; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 83.9 MPa | 12200 psi | Calculated from mfr's report of 341 N/cm per ASTM D828 and the typical thickness |
| Film Tensile Strength at Break, TD | 44.8 MPa | 6500 psi | Calculated from mfr's report of 182 N/cm per ASTM D828 and the typical thickness |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | 50% RH; tested on 10 mil thickness sample; ASTM D257 |
| Dielectric Constant | 2.9 @Frequency 60 Hz | 2.9 @Frequency 60 Hz | ASTM D150 |
| 2.9 @Frequency 1000 Hz | 2.9 @Frequency 1000 Hz | ASTM D150 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | AC Rapid Rise; ASTM D149 |
| 47.0 kV/mm | 1190 kV/in | Full-wave Impulse; ASTM D3426 | |
| Dissipation Factor | 0.0090 @Frequency 60 Hz | 0.0090 @Frequency 60 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 220 °C | 428 °F | Electrical insulation |