- 密度 [g/cm3]: 1.7
- 吸水率 [%]: 0.09
- 缺口冲击强度: 12.7
- 弯曲强度 [MPa]: 97.0
- 弯曲模量 [MPa]: 14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | |
| Water Absorption | 0.090 % | 0.090 % | in 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 40 - 50 | 40 - 50 | ASTM D2583 |
| Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ASTM D638 |
| Flexural Strength | 228 MPa | 33100 psi | ASTM D790 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ASTM D790 |
| Compressive Strength | 207 MPa | 30000 psi | ASTM D695 |
| Izod Impact, Notched | 12.7 J/cm | 23.8 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 15.4 kV/mm | 391 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.20 mm | HB @Thickness 0.126 in | |