- 弯曲强度 [MPa]: 7.93
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | silicone property; Arlon SQA-TMS-024 | ||
| Thickness | 127 microns | 5.00 mil | side 1; Arlon SQA-TMS-003 | ||
| 165 microns | 6.50 mil | side 2; Arlon SQA-TMS-003 | |||
| 457 microns | 18.0 mil | substrate; Arlon SQA-TMS-003 | |||
| 749 microns | 29.5 mil | overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 55 | 55 | silicone property; ASTM D2240 | ||
| Tensile Strength, Ultimate | 7.93 MPa | 1150 psi | silicone property; ASTM D412 | ||
| Elongation at Break | 550 % | 550 % | silicone property; ASTM D412 | ||
| Adhesive Bond Strength | 0.0483 MPa | 7.00 psi | ASTM D624 | ||
| Tear Strength | 21.0 kN/m | 120 pli | Die B; silicone property; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | |||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | ||||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Brown | ||||