- 密度 [g/cm3]: 1.15
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 25.4 microns | 1.00 mil | |||
| 152 microns | 6.00 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 18 | 18 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 950 % | 950 % | Silicone Property; ASTM D412 | ||
| Modulus of Elasticity | 0.000517 GPa | 0.0750 ksi | Silicone Property; ASTM E 831 | ||
| Poissons Ratio | 0.50 | 0.50 | Approximately, Silicone Property | ||
| Shear Strength | 3.96 MPa | 575 psi | Arlon SQA-TMS-018 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 335 µm/m-°C | 186 µin/in-°F | Silicone Property; ASTM E 831 | ||
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | Silicone Property; Arlon SQA-TMS-022 | ||
| Maximum Service Temperature, Air | 204.0 °C | 399.2 °F | |||
| Minimum Service Temperature, Air | -136 °C | -212 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.103 - 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 15.0 - 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 4.00 - 10.0 °C | 6.00 Month @Temperature 39.2 - 50.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (g/m2) | 175 | Arlon SQA-TMS-025 | |||