- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 0.06
- 弯曲模量 [MPa]: 14.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 | ||
| Density | 1.72 g/cc | 0.0621 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.060 % | 0.060 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell E | 95 | 95 | ISO 2039/2 | ||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 | ||
| Flexural Strength | 165 MPa | 23900 psi | ISO 178 | ||
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178 | ||
| Compressive Strength | 310 MPa | 45000 psi | ISO 604 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 12.0 µm/m-°C | 6.67 µin/in-°F | ASTM E831 | ||
| CTE, linear, Transverse to Flow | 33.0 µm/m-°C | 18.3 µin/in-°F | ASTM E831 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | As Molded; ISO 75A | ||
| >= 282 °C | >= 540 °F | Post Baked; ISO 75A | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Granular | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||