- 密度 [g/cm3]: 0.0561
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0561 g/cc | 0.00203 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 1.55 MPa | >= 225 psi | Bare, min |
| >= 1.76 MPa | >= 255 psi | Stabilized, min | |
| 2.17 MPa | 315 psi | Bare, typ | |
| 2.72 MPa | 395 psi | Stabilized, typ | |
| Shear Modulus | 0.0552 GPa | 8.00 ksi | Plate Shear, W Direction, typ |
| 0.110 GPa | 16.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 0.448 MPa | >= 65.0 psi | Plate Shear, W Direction, min |
| 0.621 MPa | 90.0 psi | Plate Shear, W Direction, typ | |
| >= 0.896 MPa | >= 130 psi | Plate Shear, L Direction, min | |
| 1.17 MPa | 170 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | |