- 密度 [g/cm3]: 0.0801
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0801 g/cc | 0.00289 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 3.65 MPa | >= 530 psi | Bare, min |
| >= 4.55 MPa | >= 660 psi | Stabilized, min | |
| 4.69 MPa | 680 psi | Bare, typ | |
| 5.65 MPa | 820 psi | Stabilized, typ | |
| Compressive Modulus | 0.579 GPa | 84.0 ksi | Stabilized, typ |
| Shear Modulus | 0.0689 GPa | 10.0 ksi | Plate Shear, W Direction, typ |
| 0.138 GPa | 20.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 1.24 MPa | >= 180 psi | Plate Shear, W Direction, min |
| 1.59 MPa | 230 psi | Plate Shear, W Direction, typ | |
| >= 2.10 MPa | >= 305 psi | Plate Shear, L Direction, min | |
| 2.76 MPa | 400 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |