- 密度 [g/cm3]: 0.128
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.128 g/cc | 0.00463 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 7.58 MPa | >= 1100 psi | Bare, min |
| >= 8.83 MPa | >= 1280 psi | Stabilized, min | |
| 9.31 MPa | 1350 psi | Bare, typ | |
| 10.5 MPa | 1530 psi | Stabilized, typ | |
| Compressive Modulus | 1.13 GPa | 164 ksi | Stabilized, typ |
| Shear Modulus | 0.131 GPa | 19.0 ksi | Plate Shear, W Direction, typ |
| 0.228 GPa | 33.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 2.55 MPa | >= 370 psi | Plate Shear, W Direction, min |
| 3.17 MPa | 460 psi | Plate Shear, W Direction, typ | |
| >= 4.14 MPa | >= 600 psi | Plate Shear, L Direction, min | |
| 5.17 MPa | 750 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |