- 密度 [g/cm3]: 0.0881
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0881 g/cc | 0.00318 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 4.27 MPa | >= 620 psi | Bare, min |
| >= 5.17 MPa | >= 750 psi | Stabilized, min | |
| 5.52 MPa | 800 psi | Bare, typ | |
| 6.21 MPa | 900 psi | Stabilized, typ | |
| Compressive Modulus | 0.655 GPa | 95.0 ksi | Stabilized, typ |
| Shear Modulus | 0.0758 GPa | 11.0 ksi | Plate Shear, W Direction, typ |
| 0.131 GPa | 19.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 1.38 MPa | >= 200 psi | Plate Shear, W Direction, min |
| 1.83 MPa | 265 psi | Plate Shear, W Direction, typ | |
| >= 2.69 MPa | >= 390 psi | Plate Shear, L Direction, min | |
| 3.38 MPa | 490 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |