- 密度 [g/cm3]: 0.0561
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0561 g/cc | 0.00203 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 2.00 MPa | >= 290 psi | Bare, min |
| >= 2.24 MPa | >= 325 psi | Stabilized, min | |
| 2.34 MPa | 340 psi | Bare, typ | |
| 2.83 MPa | 410 psi | Stabilized, typ | |
| Compressive Modulus | 0.283 GPa | 41.0 ksi | Stabilized, typ |
| Shear Modulus | 0.0365 GPa | 5.30 ksi | Plate Shear, W Direction, typ |
| 0.0779 GPa | 11.3 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 0.655 MPa | >= 95.0 psi | Plate Shear, W Direction, min |
| 0.827 MPa | 120 psi | Plate Shear, W Direction, typ | |
| >= 1.14 MPa | >= 165 psi | Plate Shear, L Direction, min | |
| 1.45 MPa | 210 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |