- 密度 [g/cm3]: 0.0352
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0352 g/cc | 0.00127 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 0.862 MPa | >= 125 psi | Bare, min |
| >= 1.00 MPa | >= 145 psi | Stabilized, min | |
| 1.14 MPa | 165 psi | Bare, typ | |
| 1.24 MPa | 180 psi | Stabilized, typ | |
| Compressive Modulus | 0.0896 GPa | 13.0 ksi | Stabilized, typ |
| Shear Modulus | 0.0207 GPa | 3.00 ksi | Plate Shear, W Direction, typ |
| 0.0414 GPa | 6.00 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 0.310 MPa | >= 45.0 psi | Plate Shear, W Direction, min |
| 0.414 MPa | 60.0 psi | Plate Shear, W Direction, typ | |
| >= 0.621 MPa | >= 90.0 psi | Plate Shear, L Direction, min | |
| 0.827 MPa | 120 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |