- 密度 [g/cm3]: 0.0513
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0513 g/cc | 0.00185 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 1.79 MPa | >= 260 psi | Bare, min |
| >= 2.07 MPa | >= 300 psi | Stabilized, min | |
| 2.34 MPa | 340 psi | Bare, typ | |
| 2.69 MPa | 390 psi | Stabilized, typ | |
| Compressive Modulus | 0.221 GPa | 32.0 ksi | Stabilized, typ |
| Shear Modulus | 0.0310 GPa | 4.50 ksi | Plate Shear, L Direction, typ |
| 0.0621 GPa | 9.00 ksi | Plate Shear, W Direction, typ | |
| Shear Strength | >= 0.758 MPa | >= 110 psi | Plate Shear, L Direction, min |
| >= 0.827 MPa | >= 120 psi | Plate Shear, W Direction, min | |
| 0.965 MPa | 140 psi | Plate Shear, L Direction, typ | |
| 1.03 MPa | 150 psi | Plate Shear, W Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |