- 密度 [g/cm3]: 0.104
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.104 g/cc | 0.00376 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 5.52 MPa | >= 800 psi | Bare, min |
| >= 6.34 MPa | >= 920 psi | Stabilized, min | |
| 7.067 MPa | 1025 psi | Bare, typ | |
| 8.14 MPa | 1180 psi | Stabilized, typ | |
| Compressive Modulus | 0.827 GPa | 120 ksi | Stabilized, typ |
| Shear Modulus | 0.0896 GPa | 13.0 ksi | Plate Shear, W Direction, typ |
| 0.159 GPa | 23.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 1.79 MPa | >= 260 psi | Plate Shear, W Direction, min |
| 2.28 MPa | 330 psi | Plate Shear, W Direction, typ | |
| >= 3.10 MPa | >= 450 psi | Plate Shear, L Direction, min | |
| 4.00 MPa | 580 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |