- 密度 [g/cm3]: 0.0721
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0721 g/cc | 0.00260 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 3.10 MPa | >= 450 psi | Bare, min |
| >= 3.65 MPa | >= 530 psi | Stabilized, min | |
| 3.79 MPa | 550 psi | Bare, typ | |
| 4.76 MPa | 690 psi | Stabilized, typ | |
| Compressive Modulus | 0.448 GPa | 65.0 ksi | Stabilized, typ |
| Shear Modulus | 0.0552 GPa | 8.00 ksi | Plate Shear, W Direction, typ |
| 0.0965 GPa | 14.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 1.03 MPa | >= 150 psi | Plate Shear, W Direction, min |
| 1.31 MPa | 190 psi | Plate Shear, W Direction, typ | |
| >= 1.79 MPa | >= 260 psi | Plate Shear, L Direction, min | |
| 2.24 MPa | 325 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |