- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.32
- 缺口冲击强度: 0.153
- 弯曲强度 [MPa]: 57.0
- 弯曲模量 [MPa]: 6.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.590 g/cc | 0.0213 lb/in³ | ASTM D1895 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Water Absorption | 0.32 % | 0.32 % | ASTM D570 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 86 | 86 | ASTM D785 |
| Tensile Strength, Ultimate | 57.0 MPa | 8270 psi | ASTM D638 |
| Elongation at Break | 0.81 % | 0.81 % | ASTM D638 |
| Tensile Modulus | 7.60 GPa | 1100 ksi | ASTM D638 |
| Flexural Strength | 81.0 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ASTM D790 |
| Compressive Strength | 198 MPa | 28700 psi | ASTM D695 |
| Poissons Ratio | 0.36 | 0.36 | ASTM D638 |
| Shear Modulus | 2.79 GPa | 405 ksi | Calculated |
| Izod Impact, Notched | 0.153 J/cm | 0.287 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.179 J/cm² | 0.852 ft-lb/in² | ASTM D256 |
| Impact | 93 | 93 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.30e+11 ohm-cm | 2.30e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.4 | 5.4 | ASTM D150 |
| Dielectric Strength | 8.50 kV/mm | 216 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.058 | 0.058 | ASTM D150 |
| Arc Resistance | 134 sec | 134 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 51.0 µm/m-°C @Temperature 40.0 - 130 °C | 28.3 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 198 °C | 388 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm | V-1 @Thickness 0.0591 in | |
| Oxygen Index | 29 % | 29 % | ASTM D2863 |
| Shrinkage | 0.37 % | 0.37 % | 72 hr, 120ºC; ASTM D1299 |