- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.26
- 断裂伸长率 [%]: 88.5
- 弯曲强度 [MPa]: 58.9
- 弯曲模量 [MPa]: 8.16
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.720 g/cc | 0.0260 lb/in³ | Apparent density per ASTM D1895 |
| Water Absorption | 0.26 % | 0.26 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0081 cm/cm | 0.0081 in/in | per ATM D955. Post shrinkage is 0.31% at 72hr 120ºC per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 79 | 79 | ASTM D785 |
| Tensile Strength, Ultimate | 58.9 MPa | 8540 psi | ASTM D638 |
| Elongation at Break | 0.83 % | 0.83 % | ASTM D638 |
| Tensile Modulus | 8.80 GPa | 1280 ksi | ASTM D638 |
| Flexural Yield Strength | 88.5 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 8.16 GPa | 1180 ksi | ASTM D790 |
| Compressive Yield Strength | 199.1 MPa | 28880 psi | ASTM D695 |
| Charpy Impact, Notched | 0.170 J/cm² | 0.809 ft-lb/in² | ASTM D256 |
| Impact | 98 | 98 | J/m Plenco drop ball test |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.35e+11 ohm-cm | 1.35e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.3 @Frequency 1e+6 Hz | 5.3 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.068 @Frequency 1e+6 Hz | 0.068 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 150 sec | 150 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 201 °C | 394 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 169 °C | 336 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 3.18 mm | V-1 @Thickness 0.125 in | |